TY - JOUR ID - 70071 TI - Polysulfone-based Anion Exchange Membranes for Potential Application in Solid Alkaline Fuel Cells JO - Journal of Renewable Energy and Environment JA - JREE LA - en SN - 2423-5547 AU - Iravaninia, Mona AU - Rowshanzamir, Sousan AD - Department of Chemical Engineering, Iran University of Science and Technology, Tehran, Iran Y1 - 2015 PY - 2015 VL - 2 IS - 2 SP - 59 EP - 65 KW - Solid Alkaline Fuel Cell KW - Anion Exchange Membrane KW - polysulfone KW - Trimethylamine DO - 10.30501/jree.2015.70071 N2 - In present research work, anion exchange membranes based on quaternized polysulfone with ammonium cation moieties (QAPSF) were prepared by chloromethylation, amination and alkalization. The chloromethylated polysulfone were characterized by 1HNMR spectroscopy and functionalization degree was determined according to peak area integration. Ion transport properties (ionic conductivity, ion exchange capacity, activation energy for ion transport) and water content associated properties (water uptake, swelling ratio, hydrated number) were measured for the prepared anion exchange membranes. The ion exchange capacity for these membranes varied from 0.96 to 1.73 meq/gr while the degree of chloromethylation increased from 82% to 143%. The membrane with IEC value of 1.73 meq/gr showed the highest ionic conductivity in the range of 15.87-34.01 mS/cm at 25-80 °C. The activation energy for ion transport, water uptake and swelling ratio of this membrane were measured to be 11.99 kJ/mol, 37.41% and 14.71%, respectively which demonstrated the reasonable performance of the prepared anion exchange membranes. Based on the obtained results, prepared anion exchange membranes could be proposed as good candidates for solid alkaline fuel cells. UR - https://www.jree.ir/article_70071.html L1 - https://www.jree.ir/article_70071_af27b9867d33511ff318d05a7b84f7c3.pdf ER -